Monel 400 is a binary alloy of nickel and copper (traces of iron, manganese, carbon and silicon). This alloy has high strength, resistance to acidic and alkaline environments, and good ductility and thermal conductivity. The Monel 400 is suitable for use in temperatures from minus to 1,000℃F (538 céim) . Ní féidir é a chruachan ach le hobair fhuar .
• UNS N04400
• ASTM B127
• AMS 4544
• BS 3072NA1
• BS 3076NA13
• qq-n -281
• DIN 17750
Bileog: Δ 0.8-36 mm; Leithead: 650-2000 mm; Fad 800-12000 mm
Píopa: φ 6-273 mm; Δ 1-30 mm; Fad 1000-8000 mm
Slat: φ 4-200 mm; Fad: 2000-6000 mm
Stráice: 0.05*5.0-5.0*250mm
Sreang: 0.01-10 mm
Monel 400 Comhdhéanamh Ceimiceach plátaí, bileoga agus rollaí
| grád | C | mangainéise | sileacan | Trumpa | copar | iarann | thú |
|---|---|---|---|---|---|---|---|
| Monel 400 | Suas le 0.30 | Suas le 2.00 | Suas le 0.50 | Suas le 0.024 | 28.00 – 34.00 | Uas 2.50 | 63.00 nóiméad |
Saintréithe tipiciúla an Monel 400
Clúdaíonn an tábla thíos tréithe tipiciúla an Monel 400.
|
sanacht |
córas méadrach |
Orinte |
|
dlús |
8.8 g/cm3 | 0.318 lb/i3 |
|
leáphointe |
1350 céim Celsius | 2460 céim Fahrenheit |
|
Fachtóir leathnaithe |
13 . 9µm / m. céim ({20-100 céim) |
7.710 uair-6orlach/orlach ({70-212 Céim f) |
|
Modulus déine |
65.3 kN/mm2 |
9471 kg |
|
Modulus leaisteach |
105-120 kN / mm2 | {15230-17405 lbf |
Monel 400 Airíonna Meicniúla Bileoga, Bileoga agus Rollaí
| fo -thionól | dlús | leáphointe | neart teanntachta | Neart táirgeachta (0.2% fritháirithe) | élagáil |
|---|---|---|---|---|---|
| Monel 400 | 8.8 g/cm³ | 1350 céim (2460 céim F) | PSI - 80, 000, MPA - 550 | Fórsa punt - 35, 000, mpa {- 240 | 40 % |
Próiseáil theirmeach
Alloy 400 Plate is a relatively soft material that accepts thermoforming into almost any shape. The thermoforming temperature range is 1200 – 2150℃F (649 – 1177℃). For high pressures, the recommended temperature range is 1700 – 2150℃F (927 – 1177℃). Temperatures as low as 1200℃F (649℃) féadfaidh sé gile a laghdú . ag obair ag teochtaí níos ísle beidh airíonna meicniúla níos airde agus méideanna gráin níos lú .
Grád coibhéiseach de 400 Bileog Monel
| caighdeánach | Werkstoff nr . | Córas na Náisiún Aontaithe | Iiosaean | Baiciléara | gabhsa | Avonno | Ein |
|---|---|---|---|---|---|---|---|
| Monel 400 | 2.4360 | N04400 | 4400 NW | Na 13 | МНЖМц28-2,5-1,5 | Nu -30 m | Iarann copair nicile |
Iarratais ar an Monel 400An
Is féidir Monel 400 a fháil go ginearálta sna réimsí seo a leanas:
Innealtóireacht Mara,
Próiseáil cheimiceach,
Próiseáil hidreacarbóin, teas
Malartóirí,
Comhlaí,
Caidéil uisce